Specification |
CAS No.: 9002-86-2;
Formula: C2h3cl;
EINECS: 1317-80-2;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Black;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 8;
300% Modulus,MPa: 15;
Tensile Strength,MPa: 25.0;
Tear Strength,Tn/mm: 90;
Elongation at Break,%: 400;
Abrasion,Mg: -;
Processing Temperature,°c: 210-235;
|