| Specification |
CAS No.: 9009-54-5;
EINECS: 31692-79-2;
Bonding Function: Instant Adhesive;
Morphology: Water Emulsion;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Glass/Aluminum Doors and Windows;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Organic Silicone;
Characteristic: Weatherability;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: Clear, White, Black, Grey or as Request;
Type: One-Component, Acetic;
Usage Temperature: +5ºC~+40ºC;
Working Temperature: -40ºC~+150ºC;
Contains White Oil: No;
MOQ: 60 Cartons;
Shelf Life: 15 Months;
Third Party Inspection: Supported;
Standard: GB16776-2005;
Customized Logo: Yes;
Customized Color: Yes;
Free Testing Samples: Yes;
Production Lead Time: 1 Week;
Payment Term: T/T, L/C, Paypal...;
Main Application: Aquarium, High-Quality Glass, Large Plate Glass;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.5±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~20 Min;
Rate of Cure (23 ºC, 50% Rh): ~ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Tensile Strength: ≥ 2.5 N/mm^2;
Elongation at Break: ~ 550%;
Application Temperature: 5-40ºC;
Shore a Hardness: ~ 50±5;
Advantage: Solvent Free;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.5±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~20 Min;
Rate of Cure (23 ºC, 50% Rh): ~ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Tensile Strength: ≥ 2.5 N/mm^2;
Elongation at Break: ~ 550%;
Application Temperature: 5-40ºC;
Shore a Hardness: ~ 50±5;
Advantage: Solvent Free;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.5±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~20 Min;
Rate of Cure (23 ºC, 50% Rh): ~ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Tensile Strength: ≥ 2.5 N/mm^2;
Elongation at Break: ~ 550%;
Application Temperature: 5-40ºC;
Shore a Hardness: ~ 50±5;
Advantage: Solvent Free;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.5±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~20 Min;
Rate of Cure (23 ºC, 50% Rh): ~ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Tensile Strength: ≥ 2.5 N/mm^2;
Elongation at Break: ~ 550%;
Application Temperature: 5-40ºC;
Shore a Hardness: ~ 50±5;
Advantage: Solvent Free;
|