| Specification |
CAS No.: 31692-79-2;
Formula: 9009-54-5;
Bonding Function: Instant Adhesive;
Morphology: Smooth Paste;
Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, High Grade Curtain Wall;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Organic Silicone;
Characteristic: Weatherability;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: White, Black, Grey, Clear or as Request;
Type: One-Component, Acetic;
Usage Temperature: +5ºC~+40ºC;
Working Temperature: -40ºC~+150ºC;
Contains White Oil: No;
MOQ: 1 Pallet (100 Cartons);
Shelf Life: 12 Months;
Third Party Inspection: Supported;
Standard: GB16776-2005;
Customized Logo: Yes;
Customized Color: Yes;
Free Testing Samples: Yes;
Production Lead Time: 1 Week;
Payment Term: T/T, L/C, Paypal...;
Applications: for Joint Sealing of High-Grade Exterior Walls;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|