Specification |
Refractoriness (℃): 650-1050c;
Feature: Long Time Materials;
Type: Thermal Insulation Materials;
Shape: Plate;
Material: Calcium Silicate;
Density: 230-850kg/M3;
Temeprature: 650-1050c;
Cao+Sio2: 87-90%;
Delivery Time: Within 20 Days;
Application: Heat Insulation;
Other Sizes: Cusotmized;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430/1600;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1500;
Bulk Density(g/cm3): 64-160;96/128;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.08;
|
Refractoriness (℃): 650-70;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Roller;
Material: Castable;
Application: Flat Glass Annealing Lehr;
Design: Customized;
Performance Feature: Long Term Used, No Thermal Bending, Smooth Surface;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1350ºC;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Type: Heat-Resistant Material;
Temperature: 1260c, 1350c, 1430c;
Certifiacte: ISO9001:2000;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|