Specification |
Refractoriness (℃): 650-1050c;
Feature: Long Time Materials;
Type: Thermal Insulation Materials;
Shape: Plate;
Material: Calcium Silicate;
Density: 230-850kg/M3;
Temeprature: 650-1050c;
Cao+Sio2: 87-90%;
Delivery Time: Within 20 Days;
Application: Heat Insulation;
Other Sizes: Cusotmized;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3 Content (%): ≥43%;
Sio2 Content (%): 50-65%;
Bulk Density G/Cm³: 2.35;
Apparent Porosity: 23%;
Fe2o3: 2%-4%;
Variation of Re-Burning Line 1400: +0.1/-0.4;
Application: Bottom of Glass Furnace;
Raw Material: Calcined Bauxite;
Cold Crushing Strength MPa: 50;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Powder;
Material: Alumina Cement;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Sand/Particles;
Material: Alpha Alumina;
Application: Slide Gate Plate Sets;Laddle Nozzle,Porous Plug;
Application 2: Refractory Castable Monolithics;
MOQ: 25 Mt;
Package: 1/1.25/1.35 Mt Per Jumbo Bag;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Powder;
Material: Alumina Cement;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|