| Specification |
Application: Blast Furnace, Cement Kiln, Ceramic Kiln, Chemical Kiln, Glass Kiln, Steel-Making Furnace;
Material: High Alumina;
Refractoriness (℃): 1580< Refractoriness< 1770;
Model No.: Sk35 Sk36 Sk37 Sk38 Sk40;
Al2O3: 45%~80%;
Sio2: 15%~45%;
Fe2o3: 1.8-2.0%;
Refractoriness Under [email protected]: 1380-1530ºC;
Apparent Porosity: 22-23%;
Refractoriness (ºC): 1580< Refractoriness< 1770;
Refractoriness: Sk35-40;
Bulk Density: 2.25-2.65g/cm3;
Thermal Linear Expansion@1000deg: 0.6%;
Type: Refractory Material;
|
Application: Blast Furnace, Cement Kiln, Ceramic Kiln, Chemical Kiln, Glass Kiln, Steel-Making Furnace;
Material: High Alumina, Alumina Block;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Shape: Brick;
Type: Refractory Material;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Application: Reverberatory Furnace;
Material: Alumina Block;
Refractoriness (℃): 1580< Refractoriness< 1770;
Product Name: Refractory Bricks High Alumina Brick;
Model Number: High Alumina Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Refractoriness Under Load (0.2MPa): Min 1420;
Color: Yellow;
Al2O3 Content (%): 48%-85%;
Feature: Long Time Materials, Top Grade, Instant Materials;
Type: Refractory Material;
Shape: Brick;
|
Application: Reverberatory Furnace;
Material: Alumina Block;
Refractoriness (℃): 1580< Refractoriness< 1770;
Product Name: Refractory Bricks High Alumina Brick;
Model Number: High Alumina Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Refractoriness Under Load (0.2MPa): Min 1420;
Color: Yellow;
Al2O3 Content (%): 48%-85%;
Feature: Long Time Materials, Top Grade, Instant Materials;
Type: Refractory Material;
Shape: Brick;
|
Application: Aluminum Electrolytic Cell Lining, Ele;
Material: Silicon Carbide (SiC);
Refractoriness (℃): 1580< Refractoriness< 1770;
Product Name: Silicon Carbide Brick;
Thermal Conductivity: 6-13.2;
Apparent Porosity: 10-21%;
Cold Crushing Strength: 60-120 MPa;
Resistance to Thermal Shock: 30-50times;
Bulk Density: 2.1-3.3G/Cm3;
Refractoriness: Super-Class (Refractoriness> 2000;
Sio2: 10%;
Sic: 35%-90%;
MGO: 0.8-1.2;
Cao: 0.34%;
Features: High Thermal Conductivity and Good Wear R;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
|