Specification |
CAS No.: 000000;
Formula: Epoxy;
EINECS: 000000;
Color: Gray;
Appearance: Liquid;
Main Raw Material: Epoxy;
Method: Spray;
Level: Primer;
Drying Method: Drying;
Substrate: Steel;
Components: Film Forming Matter;
Formation Mechanism: Non Conversion Type;
Density: About 2.3;
Volume Solids: 50±3%(After Mixing);
Recommended Membrane Amount: 80 Um;
Actual Dosage: Spraying About 0.63kg/M2;
Mixing Ratio: 10:1;
Surface Dry: ≤30 Min;
Spraying: Brush About 0.0.48kg/M2;
Hard Dry: ≤24h;
Complete Cure: ≤7D;
Best Aging Time: 20-30min(23ºC);
|
Color: Any Color;
Appearance: Liquid;
Main Raw Material: Polyurea;
Method: Spray;
Level: Finish Coat;
Drying Method: Air Drying;
Substrate: Any;
Components: Polyurea;
Formation Mechanism: Conversion Type;
Viscosity(25ºC): Equal and Less 1000MPa.S;
Function: Anticorrossion, Antiabrasion, Antiwater, Antislip;
Face Dry: 10seconds;
Smell: No Smelling, No Toxic Eco Freindly;
MPa: 12MPa;
Polyurea: Elastomer;
Primer: Make Surface Adhesion More Better;
Machines: Special Polyurea Machines;
Strength: Very Strong;
Transparent Color: Have;
|
Color: Any Color;
Appearance: Liquid;
Main Raw Material: Polyurea;
Method: Spray;
Level: Finish Coat;
Drying Method: Air Drying;
Substrate: Any;
Components: Polyurea;
Formation Mechanism: Conversion Type;
Viscosity(25ºC): Equal and Less 1000MPa.S;
Function: Anticorrossion, Antiabrasion, Antiwater, Antislip;
Face Dry: 10seconds;
Smell: No Smelling, No Toxic Eco Freindly;
MPa: 12MPa;
Polyurea: Elastomer;
Primer: Make Surface Adhesion More Better;
Machines: Special Polyurea Machines;
Strength: Very Strong;
Transparent Color: Have;
|
CAS No.: 1317-80-2;
Formula: TiO2;
EINECS: 215-282-2;
Color: Black;
Appearance: Powder;
Main Raw Material: Rutile;
Level: Finish Coat;
Drying Method: Drying;
Formation Mechanism: Conversion Type;
MOQ: 25 Metric Tons;
Material: TiO2;
Product Name: Rutile Sand;
Shape: Sand;
|
CAS No.: 1317-80-2;
Formula: TiO2;
EINECS: 215-282-2;
Color: Black;
Appearance: Powder;
Main Raw Material: Rutile;
Level: Finish Coat;
Drying Method: Drying;
Formation Mechanism: Conversion Type;
MOQ: 25 Metric Tons;
Material: TiO2;
Product Name: Rutile Sand;
Shape: Sand;
|