Specification |
Application: Aerospace, Electronics, Medical, Refractory;
Purity: 99%;
Type: Ceramic Ring;
Material: Alumina;
Density: 3.9g/cm3;
Color: Ivory;
Flexural Strength: 375 MPa;
Compressive Strength: 2500 MPa;
Thermal Conductivity: 27.5 W/M.K;
Dielectric Strength: >15 Kv/mm;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 16-220;
Usage: Ceramic, Polishing, Abrasive, Refractory;
HS Code: 2818101000;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Material: Alumina Oxide;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 16-600;
Usage: Ceramic, Polishing, Abrasive, Refractory;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Sample: Free;
Grade: a;
Use: Abrasive & Refractory;
MSDS: Yes;
SGS: Yes;
Delivery Time: 10 Days;
Material: Alumina Oxide;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 0.1-1, 1-3, 3-5, 5-8;
Usage: Ceramic, Polishing, Abrasive, Refractory;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Packing: 25kg;
Sample: Free;
Grade: Top Grade;
Origion: China;
Appearace: White Granular;
Material: Alumina Oxide;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 0.1-1, 1-3, 3-5, 5-8;
Usage: Ceramic, Polishing, Abrasive, Refractory;
HS Code: 2818101000;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Material: Alumina Oxide;
|