Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Hole Shape: Square, Circular, Triangular, Hexagonal, etc;
Holes: 100cpsi, 200cpsi, 300cpsi, etc;
Application: Tower Packing;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3 Content (%): ≥43%;
Sio2 Content (%): 50-65%;
Bulk Density G/Cm³: 2.35;
Apparent Porosity: 23%;
Fe2o3: 2%-4%;
Variation of Re-Burning Line 1400: +0.1/-0.4;
Application: Bottom of Glass Furnace;
Raw Material: Calcined Bauxite;
Cold Crushing Strength MPa: 50;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Sio2 Content: >23%;
Al2O3 Content (%): >60;
MGO Content (%): 0.2;
Refractoriness (Degree): 1580< Refractoriness< 1770;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Coke Oven Repair,Glass Furnace;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 2.6;
Permanent Linear Change %: 0~+0.2;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3 Content (%): ≥43%;
Sio2 Content (%): 50-65%;
Bulk Density G/Cm³: 2.35;
Apparent Porosity: 23%;
Fe2o3: 2%-4%;
Variation of Re-Burning Line 1400: +0.1/-0.4;
Application: Bottom of Glass Furnace;
Raw Material: Calcined Bauxite;
Cold Crushing Strength MPa: 50;
|
Refractoriness (℃): 800-1500;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Castable;
|