Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Material: Al-Zr-C;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 45%~80%;
Sio2: 15%~45%;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35-40;
Apparent Porosity: 22-23%;
Bulk Density: 2.25-2.65g/cm3;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Powder;
Material: Alumina Cement;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Aggregate and Powder;
Material: Bauxite Ore;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|
Classification: Sintered Magnesia Brick;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Feature: Long Time Materials;
Type: Refractory Material;
Material: MGO;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 15-16%;
Bulk Density: 2.9-3.0;
Cold Crushing Strength: 55-80MPa;
Thermal Shock Resistance Air Cool: 10;
MGO: 92-97.5%;
Cao: 1.2-2.5%;
Sio2: 0.6-3.5%;
|