| Specification |
Feature: Chemical Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
|
Production Process: Grit / Powder/ Grain;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grit / Powder/ Grain;
Used: Refractory Stone, Castable, Nozzle Material;
Color: White;
Name: White Fused Alumina;
Customized: OEM/ODM;
Other Name: White Corundum;
Nao2: <0.4;
Hardness: Superabrasive;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Fusion Method;
Refractoriness (℃): Refractoriness> 2000;
Shape: Grit / Powder/ Grain;
Chemical Al2O3 %: Min: 99.5, Typical Value 99.6;
Fe2o3 %: 0.1 Max;
Sio2: 0.1 Max;
Na2o: 0.35 Max;
Cao: 0.30 Max;
Apparent Porosity: 5 Max;
Bulk Density: 3.5g/cm3 Min;
Advantage: 20 Years Manufacturer, QC and Deliveryguaranteed;
Certificates: Reach, ISO9001/ISO14001/ISO18001;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Deep Fired;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: S2 Ladle Sliding Gate Plate for Flow Control;
Materials: Al2O3 Zro2 C or Al C;
Al2O3: 85% Min;
Zro2: 4% Min;
C: 3% Min;
Fire Process: Burned;
Finish Product: with Steel Can and Belt;
Semi-Finished Products: Available;
Rough Brick: Available;
Application: Continuous Casting Flow Control;
Usage Area: Steel Iron Industry;
Function: Control The Flow Rate of Molten Steel;
Type: Steel Making Ladle Bottom Refractory;
Slide Gate Mechansim: Available;
Service Life Performance: 4-8 Times;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Pressing;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: High Temperature Burned Ladle Sliding Gate Plate C;
Material: Al2O3+Zro2+C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|