Specification |
Material: Al-Zr-C;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
Feature: Long Time Materials;
Type: Refractory Material;
|
Material: Zircon, Aluminate Silicate;
Refractoriness (℃): 1260c-1430c;
Shape: Block;
Temperature: 1260c, 1350c, 1430c;
Density: 180-220kg/M3;
Tensile Strength: 0.04 MPa;
Permanent Linear Change in Heating %: Belowe -3;
Al2O3: 46-54%;
Al2O3+Sio2: 99%;
Zro2: 1430c: 15-17%;
Fe2o3: Below 0.2%;
Na2o+K2o: Below 0.2%;
MOQ: 1ton;
Color: White;
Package: with Pallets;
Application: Thermal Insulation, Furnance, Furnance Lining;
Industry: Petrochemical, Metallurgical, Ceramics, Glass;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
|
Material: Zirconia-Corundum;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block;
Usage: Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Type: Refractory Material;
Al2O3: 47%~72%;
Fe2o3: ≤0.5%;
Bulk Density: ≥2.95g/cm3;
Apparent Porosity: ≤17%;
Feature: Long Time Materials;
|
Material: Zirconia-Corundum;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block;
Usage: Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Type: Refractory Material;
Al2O3: 47%~72%;
Fe2o3: ≤0.5%;
Bulk Density: ≥2.95g/cm3;
Apparent Porosity: ≤17%;
Feature: Long Time Materials;
|
Material: Zirconia-Corundum;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block;
Usage: Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Type: Refractory Material;
Al2O3: 47%~72%;
Fe2o3: ≤0.5%;
Bulk Density: ≥2.95g/cm3;
Apparent Porosity: ≤17%;
Feature: Long Time Materials;
|