Specification |
CAS No.: 32131-17-2;
Formula: [-Nh(CH2)6-Nhco(CH2)4co]N-;
EINECS: None;
Molecular Principal Chain: [-Nh(CH2)6-Nhco(CH2)4co]N-;
Color: Black;
Delivery Time: 3-7 Working Days;
Grade: Virgin/ off-Grade;
Usage: Injection Moulding;
|
CAS No.: Not Applicable;
Formula: Not Applicable;
EINECS: Not Applicable;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Transparent;
Appearance: Transparent viscous liquid;
Color,(Fe/Co): 0;
Viscosity, cps. (@60ºC): 17000~35000;
Nco%: <0.1;
Oligomer, wt.%: 100;
Functionality: 2;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 63-86;
Density,g/cm3: 1.06-1.12;
100% Modulus,MPa: 2.5-6;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 9-20;
Tear Strength,MPa: 35-75;
Elongation at Break,%: 700-950;
Tear Strength,Kn/M: 35-75;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 82-96;
Density,g/cm3: 1.12;
100% Modulus,MPa: 7-10;
300% Modulus,MPa: 14-19;
Tensile Strength,MPa: 38-50;
Tear Strength,MPa: 90-130;
Elongation at Break,%: 350-500;
Tear Strength,Kn/M: 90-130;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|