Specification |
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Material: Boron Nitride;
Type: Ceramic Rings;
Color: White;
Thermal Shock Resistance: __;
Water Absorption: 0;
Processing Service: Moulding;
Density: 2.2-2.3G/Cm3;
Compressive Strength: 287 MPa;
Volume Resistivity: 10^8-10^13;
Maximum Use Temperature: 2400 ºC;
Flexural Strength: 100 MPa;
Vickers Hardness: Moh's=2;
Thermal Conductivity: 35 W/M.K;
|
Application: Refractory, Industrial Ceramic;
Type: Ceramic Plates;
Alumina Content: 92% Al2O3 or 95% Al2O3;
Density: 3.60-3.70g/cm3;
Water Absorption: 0;
Color: White, Ivory White;
Max Working Temperature: 1450-1500 Degree Centigrade;
Firing Temperature: 1550~1680 Degree Centigrade;
Acid Resistance: Yes;
Alkali-Resistance: Yes;
Impact Resistance: Yes;
Abrasion Resistance: Yes;
Anti-Corrosion: Yes;
OEM, ODM: Accept;
Application Industry: Mining/Cement/Power Plant/Port;
Package: Cartons + Plywood Case;
Applied Equipment: Pipe, Elbow, Hopper, Silo, Bunker, Funnel, Cyclone;
Material: Alumina Ceramic;
|
Application: Industrial Ceramic;
Type: Ceramic Tubes;
Shape: Straight, Bend, Elbow, Y-Piece;
Application Field: Pipe Fitting, Bends, Elbow, Orifice, Hopper, Cyclone;
Industry: Coal Fired Power Plant, Steel Mills, Asphalt Plants;
Advantage: Save Down-Time, Prelong Service Life;
Performance: High Wear Resistant, Corrossion Resistant, Abrasion;
Application Field 2: Cyclone, Pipe Fitting, Bends, Orifice, Bunker;
Material: Alumna Ceramics;
|
Application: Industrial Ceramic;
Alumina Content: 92% Al2O3 or 95% Al2O3;
Density: 3.60-3.70g/cm3;
Water Absorption: 0;
Color: White, Ivory White;
Max Working Temperature: 1450-1500 Degree Centigrade;
Firing Temperature: 1550~1680 Degree Centigrade;
Acid Resistance: Yes;
Alkali-Resistance: Yes;
Impact Resistance: Yes;
Abrasion Resistance: Yes;
Anti-Corrosion: Yes;
OEM, ODM: Accept;
Application Industry: Mining/Cement/Power Plant/Port;
Package: Cartons + Plywood Case;
Applied Equipment: Pipe, Elbow, Hopper, Silo, Bunker, Funnel, Cyclone;
Material: Alumina Ceramics;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic, Heat Transfer;
Type: Ceramic Balls;
Process: High Temperature Firing;
Sample: Free;
Brand: Fxsino;
Alumina: 20-90 %;
Moh: 7-8;
Compressive Strength: 100-20000 N/Particle;
Material: Alumina Ceramic;
|