Specification |
Application: Aerospace, Electronics, Medical, Industrial Ceramic;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Parts;
Shape: Customized;
Max Use Temperature: 1600°c;
Color: White;
Compressive Strength: 2300MPa;
Plated Layer: Ni,Cu,Au,etc;
Processing Service: Moulding;
Coaing Thickness: 8-30um;
Flexural Strength: 358MPa;
Coaing Layer: Mo/Mn;
Plating Thickness: 3-9um;
|
Application: Industrial Ceramic;
Type: Ceramic Plates;
Color: Yellow, White, Black, Gray;
Material: Alumina Ceramic;
|
Application: Structure Ceramic, Industrial Ceramic;
Type: Blade;
Shape: Comb, Teeth;
Color: White, Black, Yellow, Gold;
Feature: High Hardness, Good Wear Resistance, High Toughnes;
Nos of Teeth: 6, 10, 18, 25, 28, 30;
Use: Wahl Andis Oster Kemei;
Material: Zirconia Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Product Name: Thermal Analysis Carbon Cup;
Temperature: 1250~1370;
Test Time: 60s;
Carbon Equivalent: 3.2%-4.8%;
Carbon Content: 2.3%-4.2%;
Silicon Content: 0.6%-3.8%;
Material: Sand;
|
Color: White, Gray, Light Yellow;
Channels Density: 10~60;
Porosity: 80~90%;
Max Operation Temperature: 1100-1600 ºC;
Heat Resistance (1100-20°c): 6 Times/1100°c;
Raw Material: Alumina Silicon Carbide Zirconia;
Bending Strength: 0.6-1.0 MPa;
Heat Conductivity: 0.6-1.2 MPa;
|