Specification |
Application: Aerospace, Electronics, Medical, Refractory, High Temperature/ High Vacuum Welding;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation, High Strength;
Type: Ceramic Parts;
Treatment: Glazed, Polishing;
Color: White+Metal;
Coating Thickness: 8-30μm;
Plated Layer: Nickel/Copper/Gold;
Processing Service: Welding, Moulding;
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
|
Application: Structure Ceramic, Industrial Ceramic;
Speciality: High Strength;
Type: Ceramic Rods;
Density: 2.6g/cm3;
Working Temperature: 800c;
Size: as Per Request;
CNC: Yes;
OEM: Yes;
Usage: Electrical or Thermal Insulator;
Metallized: Available;
Keyword: Macor Machinable Glass Ceramic Blank Rod;
Material: Machinable Glass Ceramic;
|
Type: Ceramic Plates;
Commodity: Abrasion Resistant Steel Metal Backed Rubber Alumi;
Material: Alumina Ceramic;
|
Application: Ceramic Decorations, Refractory, Refractory, Structure Ceramic, Industrial Ceramic, Non-Ferrous, Alumina Making Iron Smelting Steel Ma;
Type: Ceramic Plates;
Color: White, Gray, Light Yellow;
Channels Density: 10~60;
Porosity: 80~90%;
Max Operation Temperature: 1100-1600 ºC;
Heat Resistance (1100-20°c): 6 Times/1100°c;
Raw Material: Alumina Silicon Carbide Zirconia;
Bending Strength: 0.6-1.0 MPa;
Heat Conductivity: 0.6-1.2 MPa;
Shape: Round, Square;
Material: Alumina Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic, Non-Ferrous, Alumina Making Iron Smelting Steel Ma;
Type: Ceramic Plates;
Color: White, Gray, Light Yellow;
Channels Density: 10~60;
Porosity: 80~90%;
Max Operation Temperature: 1100-1600 ºC;
Heat Resistance (1100-20°c): 6 Times/1100°c;
Raw Material: Alumina Silicon Carbide Zirconia;
Bending Strength: 0.6-1.0 MPa;
Heat Conductivity: 0.6-1.2 MPa;
Shape: Round, Square;
Material: Alumina Ceramic;
|