| Specification |
Carrier: LDPE;
Color: Red;
Application: Blowing/Injection Molding/P;
Appearance: Small Granule;
Movability Resistance: 6-8;
Color Intensity: 95-105%;
95-105%: 4-6;
Light Fastness(Level): Level 5;
|
Carrier: PE;
Color: White;
Density: 0.941 - 0.960 G/Cm;
Application/Usage: Film, Caps, Handle, Bottle, Yarn, Bag, Pipe, Toy;
Plastic Forming Method: Injection;
Melt Index, I2.16: 2.0 G/10 Min (ASTM D 1238);
Melting Point: 124°c (Equate);
Bulk Density: 530 Kg/M³ (ASTM D 1895);
Gauge: 25 Microns;
Tensile Strength @ Break (MD, Td): 31, 23 MPa (ASTM D 882);
1% Secant Modulus (MD, Td): 195, 220 MPa (ASTM D 882);
Elmendorf Tear (MD, Td): 31, 124 N/mm (ASTM D 1922);
Dart Impact, F50: 90 G (ASTM D 1709 a);
Puncture Energy: 60 J/mm (Equate);
Haze: 13% (ASTM D 1003);
Gloss, 45°: 55 (ASTM D 2457);
Efdc-7050: a Linear Low-Density Polyethylene (LLDPE) Resin Fo;
|
Carrier: PE;
Color: White;
Melt Flow Index, I 21.6: 10 G/10 Min (ASTM D1238);
Density at 23°c: 0.952 G/Cm³ (ASTM D792);
Melting Point: 131°c (Equate);
Bulk Density: 560 Kg/M³ (ASTM D1895);
Dart Impact, F 50: 170 G (ASTM D1709 a);
Elmendorf Tear (MD, Td): 70, 150 N/mm (ASTM D1922);
1% Secant Modulus (MD, Td): 1220, 1470 MPa (ASTM D882);
Tensile Strength @ Break (MD, Td): 60, 57 MPa (ASTM D882);
Elongation (MD, Td): 380, 550 % (ASTM D882);
High Film Strength and Rigidity: HDPE 6888 Has Been Optimized to Provide High Film;
Excellent Bubble Stabilit: HDPE 6888 Offers Excellent Bubble Stability at Hig;
High Extrusion Rates: The Broad Molecular Weight Distribution of HDPE 68;
Versatility: Films Produced From HDPE 6888 Are Suitable for a V;
Suitable for Non-Pressure Pipes: in Addition to Film Applications, HDPE 6888 Is ALS;
|
Carrier: PE;
Color: White;
Melt Flow Index, I 21.6: 10 G/10 Min (ASTM D1238);
Density at 23°c: 0.952 G/Cm³ (ASTM D792);
Melting Point: 131°c (Equate);
Bulk Density: 560 Kg/M³ (ASTM D1895);
Dart Impact, F 50: 170 G (ASTM D1709 a);
Elmendorf Tear (MD, Td): 70, 150 N/mm (ASTM D1922);
1% Secant Modulus (MD, Td): 1220, 1470 MPa (ASTM D882);
Tensile Strength @ Break (MD, Td): 60, 57 MPa (ASTM D882);
Elongation (MD, Td): 380, 550 % (ASTM D882);
High Film Strength and Rigidity: HDPE 6888 Has Been Optimized to Provide High Film;
Excellent Bubble Stabilit: HDPE 6888 Offers Excellent Bubble Stability at Hig;
High Extrusion Rates: The Broad Molecular Weight Distribution of HDPE 68;
Versatility: Films Produced From HDPE 6888 Are Suitable for a V;
Suitable for Non-Pressure Pipes: in Addition to Film Applications, HDPE 6888 Is ALS;
|
Carrier: PE;
Color: White;
Melt Flow Index, I 21.6: 10 G/10 Min (ASTM D1238);
Density at 23°c: 0.952 G/Cm³ (ASTM D792);
Melting Point: 131°c (Equate);
Bulk Density: 560 Kg/M³ (ASTM D1895);
Dart Impact, F 50: 170 G (ASTM D1709 a);
Elmendorf Tear (MD, Td): 70, 150 N/mm (ASTM D1922);
1% Secant Modulus (MD, Td): 1220, 1470 MPa (ASTM D882);
Tensile Strength @ Break (MD, Td): 60, 57 MPa (ASTM D882);
Elongation (MD, Td): 380, 550 % (ASTM D882);
High Film Strength and Rigidity: HDPE 6888 Has Been Optimized to Provide High Film;
Excellent Bubble Stabilit: HDPE 6888 Offers Excellent Bubble Stability at Hig;
High Extrusion Rates: The Broad Molecular Weight Distribution of HDPE 68;
Versatility: Films Produced From HDPE 6888 Are Suitable for a V;
Suitable for Non-Pressure Pipes: in Addition to Film Applications, HDPE 6888 Is ALS;
|