Specification |
CAS No.: 9004-65-3;
Color: Sub-White, White;
Appearance: Powder;
Main Raw Material: Refined Cotton;
Method: Spray;
Level: Primer;
Drying Method: Drying;
Substrate: Ceramic;
Components: Film Forming Matter;
Formation Mechanism: Conversion Type;
Model No.: HPMC;
pH: 5-8;
Bulk Density: 0.40-0.70 g/cm3;
Ash Content: 3-10%;
Particle Size: 98.5% Passes Through 100 Mesh;
Viscosity: 60000-200000;
|
Color: White;
Type: Decorative Plasterboard;
Ceiling Tile Shape: Irregular;
Surface Treatment: Film Coating;
Function: Integrated Ceiling, Fireproof Board Ceiling, Normal Ceiling, Mould-Proof Ceiling, Waterproof Ceiling, Moisture-Proof Ceiling, Soundproof Ceiling;
Feature: Artistic Ceilings;
Pattern: Without Pattern;
Application: Hotel, Office, Household, Public;
|
Color: Blue;
Appearance: Powder;
Main Raw Material: Epoxy;
Method: Spray;
Level: Finish Coat;
Drying Method: Drying;
Substrate: Steel;
Components: Pigment;
Formation Mechanism: Conversion Type;
Production Name: Metallic Sparkling Shiny Red Powder Coating Paint;
Gloss: High Glossy;
Thickness: 60-80um;
Adhesion: 0 Grade;
Hardness: 2h;
Anti Corrition: 500h;
Package: 25kg/Carton;
Storage Condition: at About 25 Degree and at Ventilated Indoors;
Curing: 180 Degree/15mins, 200 Degree/10mins;
Expiration: 12 Months;
Store: in Ventilated, Dry, Temperature < 25ºC;
Bending Test: 5mm;
Spray Ratio: 90%;
Impact Resistance: 50kg/Cm;
Coverage: 8-10 Square Meters Per Kg;
|
Color: Blue;
Appearance: Powder;
Main Raw Material: Epoxy;
Method: Spray;
Level: Finish Coat;
Drying Method: Drying;
Substrate: Steel;
Components: Pigment;
Formation Mechanism: Conversion Type;
Production Name: Metallic Electrostatic Epoxy Polyester Powder Coat;
Gloss: 90-110%;
Thickness: 60-80um;
Adhesion: 0 Grade;
Hardness: 2h;
Expiration: 12 Months;
Anti Corrition: 500h;
Package: 25kg/Carton;
Storage Condition: at About 25 Degree and at Ventilated Indoors;
Curing: 180 Degree/15mins, 200 Degree/10mins;
|
CAS No.: 25265-77-4;
Formula: C12h24o3;
EINECS: 246-771-9;
Color: Pure;
Appearance: Liquid;
Main Raw Material: Epoxy;
Method: Dip;
Level: Finish Coat;
Drying Method: Drying;
Substrate: Glass;
Components: Solvent;
Formation Mechanism: Conversion Type;
|