| Specification |
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Granular;
Material: Bauxite Ore;
Application: Refractory Abrasive Chemicals and High Aluminum CE;
Al2O3: 85%Min;
Fe2o3: 2.5%Max;
Size: 0-100mm;
Bulk Density: 2.9 Min;
Moisture (%): <0.5%;
Appearance: Granular or Powder;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Synthetic Material;
Application Area: Preheating Zone/Safety Zone;
Bulk Density: 2.2;
Apparent Porosity%: 16;
Tsr: 16 Cycle;
CCS: 57;
Alkali Resistance: 1st Grade;
Size: Customer Made;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Material: Alumina Block;
Place of Origin: Pingxiang Chemshun Plant,China;
Materials: Alumina Ceramics;
Alumina Conent: 92% Al2O3 or 95% Al2O3;
Density: 3.60-3.70 g/cm3;
Application: as Wear Resistance Part for Protection Equipments;
Application Method: Rubber Backed Ceramic, Lining Ceramic,Vulcanized C;
Application Equipment: Hopper, Chute, Conveyer, Bunker, Concrete Storage;
Application Industry: Mining Industry, Power Plant, Steel Plant,Cement P;
Sample & Store: Available;
Water Absorption: 0%;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
colour: Dark-gray;
model number: SISIC;
SiC Content (%): 83.66%;
Density: under 3.02 g/cm3;
Open Porosity: <0.1%;
Bending strength: 250MPa/280MPa;
Modulus of Elastictiy: 330Gpa/300Gpa;
Thermal Conductivity: 45W/m.K(1200 Celsius);
Coefficiant of Thermal Expansion: 4.5K-1*10-6;
Moh"s Hardness: 9.15;
Vickers Hardness HV: 20Gpa;
Acid Alkaline-proof: Excellent;
Size: Customer's Required;
|
Refractoriness (℃): 1550;
colour: darkgray;
model number: SIC;
SiC Content (%): 90%;
Density: 2.75 g/cm3;
Refractoriness: 39SK;
Refractoriness under load: 1750 Degrees;
Modulus of Rupure at room temp: 500kg/cm2;
Modulus of Rupure at 1400: 550kg/cm2;
Compressive strength: 1300kg/cm2;
Thermal Expansion at 1000 degree: 0.42-0.48%;
Apparent Porosity: 7-8%;
Thermal conductivity at 1000 degree: 13.5-14.5Kcal/m.hr.degree;
Length: Customer's Required;
Width: Customer's Required;
Thickness: Customer's Required;
|