Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Molten Steel Pouring Control Material;
Shape: Funnel, Sleeve, Round and Square Tube, Spider,etc.;
Material: Flint Clay , Bauxite ,Andalusite ,Mullite;
Application: Fourdry Industry, Bottom Pouring System;
Bulk Density: 2100-2350 Kg/M3;
Features: Low Sticking of Refractory and Steel After Use;
Cold Crushing Strength: 30-40 MPa;
|
Refractoriness (℃): 950-1450ºC;
Feature: Insulation Materials;
Type: Heat-Resistant Material;
Shape: Paper;
Material: Alumina Silica;
Color: White;
Al2O3: 47%;
Sio2: 51%;
Density: 200kg/M3;
Max Working Temperature: 1100c;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block, Zirconia Corundum;
Sio2 Content: 14.5;
Al2O3 Content (%): Min 80%;
MGO Content (%): 0.8-1.2;
Refractoriness (Degree): Common (1580°< Refractoriness< 1770°);
Cro Content (%): 1.2-1.4;
Standard Size: 230*114*65mm;
Application: Insulation,Refractory Liner;
Fe2o3 %: 1.0;
Zro2: Min 33%;
Bulk Density g/cm3: 2.3-2.4kg/M3;
Permanent Linear Change %: 0~+0.2;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35,Sk36,Sk37,Sk38,Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Sio2 Content: 50%~65%;
Al2O3 Content (%): 38-42%;
MGO Content (%): 0.8-1.2;
Refractoriness (Degree): 1580< Refractoriness< 1770;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Insulation,Refractory Liner;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 2.3-2.4kg/M3;
Permanent Linear Change %: 0~+0.2;
|