| Specification |
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1260-1600 ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2, Cr2o3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Double- Needled;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Regular Size in mm: 7320 * 610/1220 * 25mm, 3660 * 610/1220 *;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Application: Furnace Hot Face Repairs, Boiler Insulation;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Woven;
Kind: High Purity Ceramic Fiber;
Color: White;
Diameter: 6mm-120mm;
Length: 30m;
Reinforced Material: Glass Fiber or Steel Wire;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Length: 1200mm;
Width: 1000mm;
Min Thickness: 3mm;
Std Thickness: 10mm 12mm 15mm 20mm 25mm 30mm 50mm 100mm;
Density: 220kg/M3 -350kg/M3;
Color: White;
Shapes: Can Be Cut to Any Shapes;
Loss of Ignition, Loi, %: <8%;
Types: Inroganic Type and Organic Type;
Shrinkage, %,: <3;
Compressive Strength,: >0.2;
Thermal Conductivity, W/M•K: 0.03-0.18;
Grad: Bio Soluble;
Refractory Grade: Non-Inflammable;
Application: Oven, Furnace, Boiler, Stove Heat Insulation Liner;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Needle;
Kind: High Purity Ceramic Fiber;
Width: 610mm/1220mm;
Length: as Your Request;
Density: 96kg/M3, 128kg/M3;
Temperature: 1050c - 1430 C;
Color: White;
Melting Point: 1760c;
Tensile Strength: >30kpa;
Fiber Diameter (Um): 3-5;
Shrinkage (24 Hours ): ≤2.5 (1000°c);
Shot Content (Φ≥0.212mm) (%): <15;
Thermal Conductivity (W/M·K): 0.035-0.18;
Shapes: Any Shape Can Be Cut;
Smell: No Smell;
Inorganic: No Binder;
Refractory Grade: Non-Inflammable;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1400℃, 1260℃, 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Temperature: 1260c, 1350c, 1430c;
Certifiacte: ISO9001:2000;
|