Specification |
Material: Chromium;
Content: 1-25%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Casting;
Size: 10-150mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-68HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|
Material: Alumina;
Content: >90%;
Usage: Machinery, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
|
Material: Yttria Stabilized Zirconia;
Usage: Machinery, Grind, Pigment, Paint;
Processing Type: Rolling or Isostatic Pressing;
Size: 0.1~25mm;
Color: White;
Customized: Customized;
Featrue: Highest Impact Strength and Wear Resistance;
Application: Fine Grinding, Polishing;
Field: Chemical, Paints, Inks, Dyes, Coating, Textile, Pi;
OEM: Accept;
Specific Gravity: 4.0~4.2g/cm3;
Vickers Hardness: 1000~1050;
Application Industry: Chemical, Paints, Inks, Dyes, Coating, Textile, Pi;
|
Material: Sponge;
Content: >90%;
Usage: Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: Orange, White, Black or Yellow;
Customized: Customized;
Application: Polishing, Grinding, Finishing;
Thread Size: M14 or M16;
|
Material: Alumina;
Content: >90%;
Usage: Grind;
Processing Type: Rolling Type;
Size: Big;
Color: White;
Customized: Customized;
Shape: Ball;
High Alumian Conte: 90-99%;
Water Absorpt: <0.001;
Abrasion Loss: <0.15;
|