| Specification |
Material: Chromium;
Content: 1-16%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material, Mines;
Processing Type: Casting;
Size: 17-120mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-66HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|
Material: Ceramics;
Content: 85%;
Usage: Machinery, Grinding Media;
Processing Type: Rolling Type;
Size: Small;
Color: Black;
Customized: Non-Customized;
Shape: Round and Cylindrical;
Sample: Availabale;
Composition: Zirconia Oxide, Ceria Oxide;
Density: 6.15g/cm3;
Bulk Density: 3.75kg/L;
Sphericity: 98%;
Bending Strength: 1000MPa-1200MPa;
Regular Size: 0.6mm-3mm;
Vickers Hardness: 1180hv;
Crushing Strength: 70kgf(1.5mm);
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|