Specification |
Material: Chromium;
Content: 1-25%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material, Mines;
Processing Type: Casting;
Size: 10-150mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-66HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|
Material: Steel;
Content: >90%;
Usage: Machinery, Grind, Mining;
Processing Type: Hot Rolling;
Size: Middle;
Color: Black;
Customized: Customized;
Hardness: 55-65HRC;
Breakage Rate: <1%;
Impact Toughness: >12ak.J/Cm2;
Loss Roundness Rate: <1%;
Microstructure: M+C;
Heat Treatment: Quenching/Tempering;
Used: Industries of Cement Building Material, Metallurgi;
|
Material: Alumina;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Sphericity: 92%;
Fe2o3(%): <0.25;
Sio2(%): <5;
Other: <3%;
Mohs Hardness: 9;
Bulk Density(g/cm3): >3.6;
Wear Lossrate(G/Kgh): <0.1;
Diameter Size: 0.5-60mm;
Water Absorption: <0.01;
Crushing Strength(3mm): >1050n;
Application: Ball Mill,Stirred Mill, Splittings Machine;
Feature: Low Wear Loss, High Hardness;
|
Material: Alumina;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >92;
Fe2o3(%): <0.25;
Sio2(%): <5;
Mohs Hardness: 9;
Water Absorption: <0.01;
Bulk Density(g/cm3): >3.6;
Wear Loss(G/Kgh): <1.6;
Crushing Strength(3mm): >1050n;
Diameter: 0.5-60mm;
Sphericity: >95%;
|
Material: Alumina;
Content: 60% ~ 65%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >60;
Fe2o3(%): <0.6;
Sio2(%): <3.1;
Mohs Hardness: 7;
Water Absorption: <0.01;
Bulk Density(g/cm3): >2.8;
Wear Loss(G/Kgh): <1.6;
Crushing Strength(3mm): >600n;
Diameter: 0.5-13mm;
Sphericity: >95%;
|