Specification |
Material: Chromium;
Content: 1-16%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material, Mines;
Processing Type: Casting;
Size: 17-120mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-66HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|
Material: Alumina;
Content: >90%;
Usage: Grind;
Processing Type: Rolling Type & Pressing Type;
Size: 30mm,40mm,50mm,60mm;
Color: White;
Equivalent Wear Loss: 0.001%;
Density: 3.65g/cm3;
Hardness: 9 Mohs;
Anti-Compression Strength: 2000MPa;
Al2O3: >=92%;
Fe2o3: <=0.01%;
Water Absorption: 0.01%;
Sio2: 4.51%;
|
Material: Alumina;
Content: >90%;
Usage: Grind;
Processing Type: Rolling Type & Pressing Type;
Size: 30mm,40mm,50mm,60mm;
Color: White;
Equivalent Wear Loss: 0.001%;
Density: 3.65g/cm3;
Hardness: 9 Mohs;
Anti-Compression Strength: 2000MPa;
Al2O3: >=92%;
Fe2o3: <=0.01%;
Water Absorption: 0.01%;
Sio2: 4.51%;
|
Material: Zirconia;
Content: 95%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Grinding Ball;
Size: Small;
Color: White;
Customized: Customized;
Density: >3.2g/cm3;
Bulk Density: >2.0g/cm3;
Hardness: ≥9;
Abrasion: 2ppm%;
|
Material: Zirconia;
Content: 95%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Grinding Ball;
Size: Small;
Color: White;
Customized: Customized;
Density: >3.2g/cm3;
Bulk Density: >2.0g/cm3;
Hardness: ≥9;
Abrasion: 2ppm%;
|