Specification |
Standard: GB;
Application: Construction Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Plate;
Color: White;
Content: 92% Alumina;
Size: 150*150, 250*250,300*300,500*500;
Shape: Square, Hexagon, Semi-Hexagon;
Style: Dotted or Plain;
Thickness: 3mm~15mm;
Usage: Wear Resistant Used in Pulley Lagging;
Samples: Free Samples Can Be Provided;
MOQ: 50kg;
Package: PP Bags and Wooden Pallet;
Delivery Time: 15~25 Days as Your Request;
Market: Australia, USA, South Africa, Russia...;
Payment: T/T or L/C;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|