Specification |
Material: Steel;
Content: 73-94%;
Usage: Machinery, Chemical, Grind;
Processing Type: Forged/Hot Rolled and Casting;
Size: Dia: 10-60mm Length: 15-80;
Color: Black;
Customized: Customized;
Which Port: Qingdao, Shandong Province, China;
Shape: Cylinder;
Hardness: 45-65HRC;
Impact Toughness: >4ak.J/Cm2;
Breakage Rate: <1%;
Heat Treatment: Quenching and Tempering;
|
Material: Alumina;
Content: >90%;
Usage: Grind;
Processing Type: Isostatic Pressing Type;
Size: 30mm,40mm,50mm,60mm;
Color: White;
Equivalent Wear Loss: 0.001%;
Density: 3.65g/cm3;
Hardness: 9 Mohs;
Anti-Compression Strength: 2000MPa;
Al2O3: >=92%;
Fe2o3: <=0.01%;
Water Absorption: 0.01%;
Sio2: 4.51%;
|
Material: Zirconia;
Content: >90%;
Usage: Grind;
Processing Type: Isostatic Pressing Type;
Size: Small;
Color: White;
Customized: Customized;
Item: Zirconia Grinding Balls;
Materials: Zirconia;
Type: High-Zironia;
Diameter: 1mm-70mm;
Grinding Situation: Dry Grinding , Wet Griding;
Feature: High Hardness, High Density and Anticorrosion;
Application: Ball Mill, Pebble Mill, Strilled Mill;
Field: Ceramic,Metallurgy, Glass, Porcelain, Enamel;
OEM: Accept;
|
Material: Alumina;
Content: 65%~95%;
Usage: Chemical, Grind;
Processing Type: Rolling & Pressing;
Size: 30/40/50/60/70 mm;
Color: White;
Customized: Can Be Customized;
Equivalent Wear Loss: 0.001%;
Density: 3.65g/cm3;
Hardness: 9 Mohs;
Anti-Compression Strength: 2000MPa;
Al2O3: >=92%;
Fe2o3: <=0.01%;
Water Absorption: 0.01%;
Sio2: 4.51%;
|
Material: Zirconia Ceramic;
Content: 75% ~ 80%;
Usage: Machinery, Chemical, Grind;
Processing Type: Rolling Type;
Size: 0.5-13 mm;
Color: White;
Customized: Customized;
Density: >4.98;
Shipping Way: Fob, CIF, DDP, DDU etc;
Certificate: ISO;
Gpa: >10;
G/Kg.H: <1.5;
Picture Product Size: Diameter 2mm,3mm;
Package: Normal or Customzied;
Function: Grinding;
Sample Time: 2-5 Days;
Bulk Order Time: 10-30 Days;
Shipping Mark: Accept;
Key Words: Grinding Ceramic Ball Media;
Shape: Ball;
Other Name: Zta Ceramic Grinding Ball;
|