Specification |
Refractoriness (℃): 1050ºC;
Feature: Long Time Materials;
Type: Calcium Silicate Boards;
Shape: Block;
Material: Sio2, Cao;
Edge: Square;
Application: Building, Furnace.etc;
Thickness: 25mm, 50mm, 100mm or Customized;
Character: Non-Asbestos;
Colour: White;
Appearance: Plate or Board;
Density: 170-300kg/M³;
Key Properties: Low Thermal Conductivity&Good Compression Strength;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Instant Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Magnesia Chrome;
MGO: 50%-85%;
Bluk Density: 2.95g/cm3-3.25g/cm3;
Apparent Porosity: 15%-17%;
Cold Crushing Sternth: 60MPa-80MPa;
Cr2o3: 6%- 28%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35,Sk36,Sk37,Sk38,Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 17;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|