Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Size: According to The Drawings;
Application: Used in Various Kinds of Industrial Furnaces;
Alumina Range: 40%-85%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Mullite;
Application Area: Transition zone and safety zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.67-2.7g/cm3;
Apparent Porosity: 17%;
Tsr 1100ºC: 10 Cycle;
Rul: 1680ºC;
CCS MPa: 90;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|