Specification |
After-sales Service: 24-Hour Online Service;
Warranty: 10years;
Material: ABS;
Kind: ABS/PMMA Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Thickness: 1.0-8.0mm;
Color: Clear, White, Color, Black or Customized;
Surface: High Gloss, Emboss, Matte;
Base Material: Acrylic+ABS PMMA/ABS;
Maximum Width: 2150mm;
|
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: <1.2%;
Tensile Strength: 12-20 MPa;
Impact Strength: 8-15kj/M2;
Bending Intensity: 12-18MPa;
Bending Elasticity Modulus: 800-900MPa;
Apparent Density: 300-900kg/M3;
Breakage Elongation: 15-20%;
Shore Hardness: 45-60;
Fire Resistance: Self-Extinguish Time Is Less Than Five Seconds;
Optional Color: White, Black, Blue, Gree, Red, Yellow, Gray, etc;
|
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: <1.2%;
Tensile Strength: 12-20 MPa;
Impact Strength: 8-15kj/M2;
Bending Intensity: 12-18MPa;
Bending Elasticity Modulus: 800-900MPa;
Apparent Density: 300-900kg/M3;
Breakage Elongation: 15-20%;
Shore Hardness: 45-60;
Fire Resistance: Self-Extinguish Time Is Less Than Five Seconds;
Optional Color: White, Black, Blue, Gree, Red, Yellow, Gray, etc;
|
After-sales Service: on Line;
Warranty: 5years;
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: <1.2%;
Tensile Strength: 12-20 MPa;
Impact Strength: 8-15kj/M2;
Bending Intensity: 12-18MPa;
Bending Elasticity Modulus: 800-900MPa;
Apparent Density: 300-900kg/M3;
Breakage Elongation: 15-20%;
Shore Hardness: 45-60;
Fire Resistance: Self-Extinguish Time Is Less Than Five Seconds;
Optional Color: White, Black, Blue, Gree, Red, Yellow, Gray, etc;
|
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: <1.2%;
Tensile Strength: 12-20 MPa;
Impact Strength: 8-15kj/M2;
Bending Intensity: 12-18MPa;
Bending Elasticity Modulus: 800-900MPa;
Apparent Density: 300-900kg/M3;
Breakage Elongation: 15-20%;
Shore Hardness: 45-60;
Fire Resistance: Self-Extinguish Time Is Less Than Five Seconds;
Optional Color: White, Black, Blue, Gree, Red, Yellow, Gray, etc;
|