Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM, AISI;
Purity: 59%;
Alloy: Alloy;
Type: Nickel Bar;
Powder: Not Powder;
Diameter: 3-300mm;
Surface: Black, Bright, Polished, Pickling;
Length: as Your Requirments;
MOQ: 100kgs;
Sample: Free-Sample;
Condition: Annealed;Heat Treatment;;
Technique: Cold Rolled, Hot Rolled;
Mtc: Cold Drawn Hot Rolled,Forged;
Stock: in Stock;
T.S.(≥ MPa): 752;
Key Words: C2000 Alloy Supplier;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|