Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Top Grade;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Refractory Bricks High Alumina Brick;
Model Number: High Alumina Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Refractoriness Under Load (0.2MPa): Min 1420;
Color: Yellow;
Application: Reverberatory Furnace;
Al2O3 Content (%): 48%-85%;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|