Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Crucible;
Material: Bn;
Max Working Temperature: 1800c;
Thermal Shock Resistance: 180-220t;
Special: According to Customer's Design;
Product: Bn Parts;
Name: Machine Bn Part;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Name: Melting Crucible for Gold Silver Cooper Aluminium;
Color: Black Grey;
Application: Industrial Ceramic;
Density: 1.9-2.1g/cm3;
Characteristic: Long Service Life;
Attribute: Wear-Resisting,High Temperature Resistance;
Working Temperature: 1800 Degree Celsius;
Usage: Melting Aluminium,Copper,Iron,etc.;
Sic Content: 98%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Name: Aluminum Copper Melting Silicon Carbide Sic Crucib;
Color: Black Grey;
Application: Industrial Ceramic;
Density: 1.9-2.1g/cm3;
Sic Content: 98%;
Characteristic: Long Service Life;
Attribute: Wear-Resisting,High Temperature Resistance;
Usage: Melting Aluminium,Copper,Iron,etc.;
Working Temperature: 1800 Degree Celsius;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Aluminum/Silicon Carbide/Zircornia/Cordierite;
Hole Shape: Square / Round / Hexagon/Triangle;
Size: 50*50*20mm, 65*65*15mm, 100*75*13mm, 81*12mm;
Outer Shape: Square, Rectangle, Round;
Working Temp.: ≤1500 Degree;
Hole Number: 100/200/300csi;
Hole Rate: 35-60%;
Bending Strength: ≥1MPa (at Normal Temperature);
Compressive Strength: ≥20MPa (at Normal Temperature);
Volume Density: 0.8-1.2g/cm3;
Customization: Yes;
|