Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Top Grade;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Refractory High Alumina Brick;
Model Number: Sk32 Sk34 Sk36 Sk38 High Alumina Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Refractoriness Under Load (0.2MPa): Min 1420;
Color: Yellow;
Application: Reverberatory Furnace;
Al2O3 Content (%): 48%-85%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|