Specification |
Fiber Type: Staple;
Product Name: Microfiber;
Length: Times of 4mm/6mm with 1mm More or Less;
Raw Material: Polypropylene;
Fiber Diameter: 20um-30um;
Tensile Strength: 450MPa Min;
Crack Elongation: 20+/-5%;
Density(g/cm3): 0.91+/-0.01;
Acid &Alkali Resistance: Strong;
Certificate 1: Ce;
Certificate 2: ISO;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Pattern: Plain;
Color: White;
Structure: Synthetic Carbon Chain;
Width: 20-30um;
Function: Concrete Reinforcement;
|
Fiber Type: Filament;
Acid & Alkaline Resistance: Strong;
Chemical Property: Stability;
Water Absorbency: No;
Density: 0.91;
Material: 100% Polypropylene;
Feature: Abrasion-Resistant, Heat-Resistant;
Pattern: Plain;
Color: White;
Function: Radiation-Resistant Fiber;
Structure: Synthetic Carbon Chain;
Usage: Refracotry;
Width: Provides Custom-Made Service;
|
Fiber Type: Filament;
Acid & Alkaline Resistance: Strong;
Chemical Property: Stability;
Water Absorbency: No;
Density: 0.91;
Material: 100% Polypropylene;
Feature: Abrasion-Resistant, Heat-Resistant;
Pattern: Plain;
Color: White;
Function: Radiation-Resistant Fiber;
Structure: Synthetic Carbon Chain;
Usage: Refracotry;
Width: Provides Custom-Made Service;
|
Fiber Type: Filament;
Acid & Alkaline Resistance: Strong;
Chemical Property: Stability;
Water Absorbency: No;
Density: 0.91;
Material: 100% Polypropylene;
Feature: Abrasion-Resistant, Heat-Resistant;
Pattern: Plain;
Color: White;
Function: Radiation-Resistant Fiber;
Structure: Synthetic Carbon Chain;
Usage: Refracotry;
Width: Provides Custom-Made Service;
|
Fiber Type: Polypropylene Fiber;
Ignition Point: 560-570ºC;
Elongation at Break: 10% Min;
Melting Point: 160 - 170;
Density: 0.91+/-0.01g/cm3;
Tensile Strength: 560MPa Min;
Length: 3-20mm;
Elastic Modulus: 3500MPa Min;
Acid, Alkali & Salt Resistance: Strong;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling;
Color: White;
Function: for Anti Crack Concrete Reinforcement;
|