Specification |
Fiber Type: Staple;
Product Name: PP Twist Fiber Macro Synthetic Fibers;
Raw Material: 100% Virgin Polypropylene;
Length: 19mm, 48mm, 54mm;
Equivalent Dia(mm): 0.3+/-0.05;
Crack Ratio: 20+/-5 %;
Tensile Strength: >600 MPa;
Elastic Modulus (MPa): >3500;
Break Tensile Ratio(%): 8-15;
Melting Point ( C. Deg): 160-170;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant, Reinforcement;
Color: Black;
Pattern: Twist;
Width: as Request;
Function: Reinforcement;
Structure: Twist;
|
Fiber Type: PP Woven;
The Width: 2 to 200cm;
The Length: as Per Your Requirement;
The Color: Any Color Available;
Material: 100% Polypropylene;
Pattern: Plain;
Function: High Strength Fiber;
Usage: Making Bags;
Feature: Recycle;
Color: Any Color Availabe;
Width: 25-150cm;
Structure: PP Woven;
|
Fiber Type: PP Woven;
Material: 100% Polypropylene;
Pattern: Plain;
Function: High Strength Fiber;
Usage: Making Bags;
Feature: Recycle;
Color: Any Color Availabe;
Width: 25-150cm;
Structure: PP Woven;
|
Fiber Type: Polypropylene Fiber;
Ignition Point: 560-570ºC;
Elongation at Break: 10% Min;
Melting Point: 160 - 170;
Density: 0.91+/-0.01g/cm3;
Tensile Strength: 560MPa Min;
Length: 3-20mm;
Elastic Modulus: 3500MPa Min;
Acid, Alkali & Salt Resistance: Strong;
Fiber Length: 3, 6, 9, 16, 20mm or Tailored;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling;
Color: White;
Function: for Anti Crack Concrete Reinforcement;
|
Fiber Type: Polypropylene Fiber;
Ignition Point: 560-570ºC;
Elongation at Break: 10% Min;
Melting Point: 160 - 170;
Density: 0.91+/-0.01g/cm3;
Tensile Strength: 560MPa Min;
Length: 3-20mm;
Elastic Modulus: 3500MPa Min;
Acid, Alkali & Salt Resistance: Strong;
Fiber Length: 3, 6, 9, 16, 20mm or Tailored;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Color: White;
Function: for Anti Crack Concrete Reinforcement;
|