Specification |
Fiber Type: Twisted Bundle;
Strength: 600 MPa Min;
Application: Concrete Reinforcement;
Length: 48mm - 54mm;
MOQ: 1000kg;
Keywords: Concrete PP Fiber;
Usage: Concrete;
Material: 100% Polypropylene;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Feature: Concrete Reinforcment;
Color: Grey;
|
Fiber Type: Staple;
Length: 20, 48, 50, 54mm Ect;
Shape: Hybrid;
Density(g/cm3): 0.91 +/- 0.01;
Equivalent Dia(mm): 0.3;
Crack Ratio: 20+/-5 %;
Product Name: High Quality Polypropylene Macrofiber;
Tensile Strength: >500 MPa;
Elastic Modulus (MPa): >3500;
Raw Material: PP;
Break Tensile Ratio(%): 8-15;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Pattern: Plain;
Width: 47/48";
Function: High Strength Fiber;
Color: Grey;
Structure: PP;
|
Fiber Type: Staple;
Length: 20, 48, 50, 54mm Ect;
Shape: Hybrid;
Density(g/cm3): 0.91 +/- 0.01;
Equivalent Dia(mm): 0.3;
Crack Ratio: 20+/-5 %;
Product Name: Concrete Fibers PP Hybrid Fiber;
Tensile Strength: >500 MPa;
Elastic Modulus (MPa): >3500;
Raw Material: PP;
Break Tensile Ratio(%): 8-15;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Pattern: Plain;
Width: 47/48";
Function: High Strength Fiber;
Color: Grey;
Structure: PP;
|
Fiber Type: Staple;
Length: 20, 48, 50, 54mm Ect;
Shape: Hybrid;
Density(g/cm3): 0.91 +/- 0.01;
Equivalent Dia(mm): 0.3;
Crack Ratio: 20+/-5 %;
Product Name: PP Hybrid Fibre 54mm for Concrete Improvement;
Tensile Strength: >500 MPa;
Elastic Modulus (MPa): >3500;
Raw Material: PP;
Break Tensile Ratio(%): 8-15;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Pattern: Plain;
Width: 47/48";
Function: High Strength Fiber;
Color: Grey;
Structure: PP;
|
Fiber Type: Staple;
Length: 20, 48, 50, 54mm Ect;
Shape: Hybrid;
Density(g/cm3): 0.91 +/- 0.01;
Equivalent Dia(mm): 0.3;
Crack Ratio: 20+/-5 %;
Product Name: PP Hybrid Fibre 54mm for Concrete Improvement;
Tensile Strength: >500 MPa;
Elastic Modulus (MPa): >3500;
Raw Material: PP;
Break Tensile Ratio(%): 8-15;
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Pattern: Plain;
Width: 47/48";
Function: High Strength Fiber;
Color: Grey;
Structure: PP;
|