Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: >98%;
Alloy: Alloy;
Type: CuNi Wire;
Powder: Not Powder;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Max Working Tem: 250c;
Resistivity: 0.15ohm/M;
Density: 8.9g/cm3;
TCR X10-6 / 0c (20~600 0c): <50;
Emf Vs Cu (μV/ 0c) (0~100 0c): -25;
Melting Point: 1100c;
|
Application: Aviation, Electronics, Industrial, Chemical;
Standard: GB, DIN, BS, ASTM, AISI;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Thickness: 0.5-20mm;
Width: 1200mm;
Length: 3000mm;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni 76%;
Characteristics: High Resistivity, Good Anti-Oxidation Resistance;
Range of Application: Resistor, Heater,Chemical;
Electrical Resistivity: 1.09 Ohm mm2/M;
The Highest Use Temperature: 1400;
Density: 8.4G/Cm3;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1200;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni 76%;
Characteristics: High Resistivity, Good Anti-Oxidation Resistance;
Range of Application: Resistor, Heater,Chemical;
Electrical Resistivity: 1.09 Ohm mm2/M;
The Highest Use Temperature: 1400;
Density: 8.4G/Cm3;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1200;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni 76%;
Characteristics: High Resistivity, Good Anti-Oxidation Resistance;
Range of Application: Resistor, Heater,Chemical;
Electrical Resistivity: 1.09 Ohm mm2/M;
The Highest Use Temperature: 1400;
Density: 8.4G/Cm3;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1200;
|