| Specification |
Usage: Concrete, Filling Material, Spinning, Non-Woven Fabric;
Material: 100% Polyester;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant;
Fiber Type: Staple;
Pattern: Plain;
Color: White;
Width: 43/44";
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Fineness: 1.5/3/4/7/15D;
Length: 25/32/38/51/64mm;
Type: Hollow;
Style: Staple;
Use: Filling Material, Non-Woven Fabric, Spinning;
Grade: Recycled/Virgin;
Application: Filling Quits/Pillows/Cushions;
Factory Place: Jisngsu, China;
Production Lines: 2 Line;
Capacity: 90000kg Per Day;
Delivery Time: 5-7 Days;
Packing Bag Colors: White/Blue/Green;
|
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Cracking;
Fiber Type: Filament;
Pattern: Plain;
Color: Grey;
Width: Monofilament;
Function: High Strength Fiber;
Structure: Reinforcing Fiber;
Length: 20, 30, 50, 54mm;
Shape: Twisted/Bunchy;
Density(g/cm3): 0.91 +/- 0.01;
Equivalent Dia(mm): 0.3;
Crack Ratio: 20+/-5 %;
Product Name: PP Twisted Bundle Fibre;
Tensile Strength: >500 MPa;
Elastic Modulus (MPa): >3500;
Raw Material: 100% Polypropylene;
Break Tensile Ratio(%): 8-15;
|
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant, Reinforcement;
Fiber Type: Staple;
Pattern: Twist;
Color: Black;
Width: as Request;
Function: Reinforcement;
Structure: Twist;
Product Name: PP Twist Fiber Macro Synthetic Fibers;
Raw Material: 100% Virgin Polypropylene;
Length: 19mm, 48mm, 54mm;
Equivalent Dia(mm): 0.3+/-0.05;
Crack Ratio: 20+/-5 %;
Tensile Strength: >600 MPa;
Elastic Modulus (MPa): >3500;
Break Tensile Ratio(%): 8-15;
Melting Point ( C. Deg): 160-170;
|
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant, Reinforcement;
Fiber Type: Staple;
Pattern: Twist;
Color: Black;
Width: as Request;
Function: Reinforcement;
Structure: Twist;
Product Name: PP Twist Fiber Macro Synthetic Fibers;
Raw Material: 100% Virgin Polypropylene;
Length: 19mm, 48mm, 54mm;
Equivalent Dia(mm): 0.3+/-0.05;
Crack Ratio: 20+/-5 %;
Tensile Strength: >600 MPa;
Elastic Modulus (MPa): >3500;
Break Tensile Ratio(%): 8-15;
Melting Point ( C. Deg): 160-170;
|
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Anti-Static, Heat-Resistant, Reinforcement;
Fiber Type: Staple;
Pattern: Twist;
Color: Black;
Width: as Request;
Function: Reinforcement;
Structure: Twist;
Product Name: PP Twist Fiber Macro Synthetic Fibers;
Raw Material: 100% Virgin Polypropylene;
Length: 19mm, 48mm, 54mm;
Equivalent Dia(mm): 0.3+/-0.05;
Crack Ratio: 20+/-5 %;
Tensile Strength: >600 MPa;
Elastic Modulus (MPa): >3500;
Break Tensile Ratio(%): 8-15;
Melting Point ( C. Deg): 160-170;
|