Specification |
CAS No.: 7085-85-0;
Formula: Mixture;
EINECS: 230-391-5;
Bonding Function: Instant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: White;
Model No.: Fa;
Shelf Life: 12months;
Cetificate: ISO, TUV, CE;
Advantage: High Yield Insulation;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.5±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~25 Min;
Rate of Cure (23 ºC, 50% Rh): ~ 2.5 mm/24hrs;
Non-Sag Properties: Good;
Tensile Strength: ≥ 1.8 N/mm^2;
Elongation at Break: ~ 300%;
Application Temperature: 5-40ºC;
Shore a Hardness: ~ 45±5;
Advantage: Solvent Free;
Origen: China;
Ventajas: Sin Dissolvetes;
Densidad: 1.5;
Tiempo De Aplicacion: 25 Minutos;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.5±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~25 Min;
Rate of Cure (23 ºC, 50% Rh): ~ 2.5 mm/24hrs;
Non-Sag Properties: Good;
Tensile Strength: ≥ 1.8 N/mm^2;
Elongation at Break: ~ 300%;
Application Temperature: 5-40ºC;
Shore a Hardness: ~ 45±5;
Advantage: Solvent Free;
Origen: China;
Ventajas: Sin Dissolvetes;
Densidad: 1.5;
Tiempo De Aplicacion: 25 Minutos;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.30±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~ 55 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Shore a Hardness: ~45;
Shear Strength: ≥ 1 N/mm^2;
Tensile Strength: ≥ 2 N/mm^2;
Elongation at Break: ~ 350%;
Tear Strength: 6 N/mm;
Origen: China;
Package: 310ml Cartucho 600ml Salchicha;
Uso: PARA Uso Interior;
|
Bonding Function: Adhesive Joint Sealing;
Morphology: Uniform Paste;
Application: Automobile, Construction;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black White Grey;
Density: 1.30±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Tack-Free Time (23 ºC, 50% Rh): ~ 55 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
Non-Sag Properties: Good;
Shore a Hardness: ~45;
Shear Strength: ≥ 1 N/mm^2;
Tensile Strength: ≥ 2 N/mm^2;
Elongation at Break: ~ 350%;
Tear Strength: 6 N/mm;
Origen: China;
Package: 310ml Cartucho 600ml Salchicha;
Uso: PARA Uso Interior;
|