Specification |
Application: Industrial Ceramic, Electronic Ceramic;
Grain Size: 1-10um;
Purity: 96%, 99.6%;
Type: Ceramic Plates;
Delivery: 30 Days;
Thermal Conductivity: Min 24 W/Mk;
Young's Modulus: 340 Gpa;
Thickness: 0.2-2mm;
Forming Method: Tape Casting;
Material: Alumina Ceramic;
|
Application: Structure Ceramic, Industrial Ceramic;
Purity: 95%;
Type: Ceramic Parts;
Name: 95% Alumina Ceramic Ignition Electrode;
Size: Customized;
Appearance: Neat;
Surface: Smooth;
Property: High Wear Resistance;
Advantage: Long Working Life;
MOQ: 1000;
Flexural Strength: 650MPa;
Shape: Customized;
Feature: Insulation;
Density: 3.85g/cm3;
Usage: Fixing;
Al2O3 Content: 95%;
Key Word: 95% Alumina Ceramic Igniter;
Material: Alumina Ceramic;
|
Application: Structure Ceramic, Industrial Ceramic;
Purity: 95%;
Type: Ceramic Parts;
Name: Alumina Ceramic Ignition Electrode;
Size: Customized;
Appearance: Neat;
Surface: Smooth;
Property: High Wear Resistance;
Advantage: Long Working Life;
MOQ: 1000;
Flexural Strength: 650MPa;
Shape: Customized;
Feature: Insulation;
Density: 3.85g/cm3;
Usage: Fixing;
Al2O3 Content: 95%;
Key Word: Al2O3 Ceramic Igniter;
Material: Alumina Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic, Machinery, Electronic, Chemical, Petroleum etc.;
Type: Ceramic Parts;
Color: White/Ivory;
Density: ≥3.7g/cm3;
Alumina Content: 92%-99.8%;
Unit: Piece;
Gas Permeability: 0;
Water Absorption: 0;
Maximum Use Temperature: ≤1650c;
Compressive Strength(20°c): 2000MPa;
Material: Alumina Ceramic;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic, Machinery, Electronic, Chemical, Petroleum etc.;
Type: Ceramic Parts;
Color: White/Ivory;
Density: ≥3.7g/cm3;
Alumina Content: 92%-99.8%;
Unit: Piece;
Gas Permeability: 0;
Water Absorption: 0;
Maximum Use Temperature: ≤1650c;
Compressive Strength(20°c): 2000MPa;
Material: Alumina Ceramic;
|