Specification |
Application: Industrial Ceramics;
Grain Size: 1-10um;
Purity: 95%;
Type: Ceramic Plate;
Delivery: 30 Days;
Thermal Conductivity: Min 24 W/Mk;
Young's Modulus: 340 Gpa;
Thickness: 0.2-2mm;
Forming Method: Tape Casting;
|
Application: Aerospace, Electronics, Medical, Industrial Ceramic;
Purity: 95%;
Type: Ceramic Plates;
Color: White/Ivory;
Water Absorption: 0;
Thermal Conductivity: 16.7-35W/M.K;
Processing Service: Moulding;
Density: 3.6-3.95g/cm3;
Compressive Strength: 550-3000MPa;
Volume Resistivity: >10 14;
Flexural Strength: 345-380MPa;
Max Using Temperature: 1500-1700;
Vickers Hardness: 11-14gpa;
|
Application: Aerospace, Electronics, Medical, High Temperature/ High Vacuum Welding;
Type: Ceramic Parts;
Treatment: Glazed, Polishing;
Color: White+Metal;
Coating Thickness: 8-30μm;
Coating Layer: Mo/Mn;
Plated Layer: Nickel/Copper/Gold etc.;
Processing Service: Moulding;
Plating Thickness: 2-9μm;
Max. Use Temperature: 1600ºC;
|
Application: Aerospace, Electronics, Medical;
Type: Electrothermal Ceramics;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial;
Purity: 95%;
Type: Ceramic Part;
Material: Alumina;
Density: 3.6g/cm3;
Color: White;
Flexural Strength: 300 MPa;
Compressive Strength: 2300 MPa;
Thermal Conductivity: 20 W/M.K;
Dielectric Strength: >15 Kv/mm;
|