Specification |
Refractoriness (℃): 1380;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
colour: Dark-gray;
model number: SISIC;
SiC Content (%): 83.66%;
Density: under 3.02 g/cm3;
Open Porosity: <0.1%;
Bending strength: 250MPa/280MPa;
Modulus of Elastictiy: 330Gpa/300Gpa;
Thermal Conductivity: 45W/m.K(1200 Celsius);
Coefficiant of Thermal Expansion: 4.5K-1*10-6;
Moh"s Hardness: 9.15;
Vickers Hardness HV: 20Gpa;
Acid Alkaline-proof: Excellent;
Size: Customer's Required;
|
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Long Time Materials, Instant Materials, Long Time Materials, Instant Materials;
Material: Soda Lime Borosilicate Glass, Soda Lime Borosilicate Glass;
Shotblast Type: Shot Blasting;
Sandblasting Type: Automatic Sandblasting;
Shotblast Application: Guns and Tanks;
Sandblasting Method: Dry Spray;
Sandblasting Applications: Metallurgy;
Shotblast Material: Glass;
Appearance: Transparent;
Density: 2.4-2.6g/cm3;
Hardness: 6-7moh's;
Roundness: >85%;
Sio2: >72%;
|
Refractoriness (℃): 1260c 1350c 1430c;
Feature: Long Time Materials, Instant Materials, Thermal Insulation Materials;
Type: Refractory Material;
Shape: Block;
Material: Ceramic Fiber;
Chemical Composition: Sio2, Al2O3;
Al2O3: ≥43/44/52/35;
Sio2: ≥54/55/47/49;
Density (Kg/M3): 160-220;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Roll;
City: Zibo;
Manufacture: Luyang;
Raw Material: Alumina Fiber;
Package: Carton Box;
Name: Alumina Fiber Blanket;
Product: Pcw Blanket;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 100 Cycle;
Rul: 1700ºC;
CCS MPa: 60;
MGO: 85-87;
|