Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical, Making Hermetic Seals;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 24-27%;
Alloy: Alloy;
Type: Nickel Bar;
Powder: Not Powder;
Density: 8.19 G/Cm;
Melting Point: 1320-1365c;
Diameter: 6~100mm;
Mean Coeff Thermal Expansion: 9.17;
Tensile: 1035MPa;
Elongation: 25%;
|
Application: Medical;
Standard: JIS, GB, ASTM;
Alloy: Alloy;
Type: Niti;
Powder: Not Powder;
Condition: Annealed;
Ti (Min): 45;
Wire Gauge: 0.08~7.0 mm;
Color: Polished, Ground, Oxide Surface;
Delivery Time: 5-15 Days;
Thermal Conductivity: 0.1 W/Cm-° C;
Heat Capacity: 0.077 Cal/GM-° C;
Latent Heat: 5.78 Cal/GM; 24.2 J/GM;
|
Application: Medical;
Standard: JIS, GB, ASTM;
Alloy: Alloy;
Type: Niti;
Powder: Not Powder;
Condition: Annealed;
Ti (Min): 45;
Wire Gauge: 0.08~7.0 mm;
Color: Polished, Ground, Oxide Surface;
Delivery Time: 5-15 Days;
Thermal Conductivity: 0.1 W/Cm-° C;
Heat Capacity: 0.077 Cal/GM-° C;
Latent Heat: 5.78 Cal/GM; 24.2 J/GM;
|
Application: Medical;
Standard: JIS, GB, ASTM;
Alloy: Alloy;
Type: Niti;
Powder: Not Powder;
Condition: Annealed;
Ti (Min): 45;
Wire Gauge: 0.08~7.0 mm;
Color: Polished, Ground, Oxide Surface;
Delivery Time: 5-15 Days;
Thermal Conductivity: 0.1 W/Cm-° C;
Heat Capacity: 0.077 Cal/GM-° C;
Latent Heat: 5.78 Cal/GM; 24.2 J/GM;
|
Application: Medical;
Standard: JIS, GB, ASTM;
Alloy: Alloy;
Type: Niti;
Powder: Not Powder;
Condition: Annealed;
Ti (Min): 45;
Wire Gauge: 0.08~7.0 mm;
Color: Polished, Ground, Oxide Surface;
Delivery Time: 5-15 Days;
Thermal Conductivity: 0.1 W/Cm-° C;
Heat Capacity: 0.077 Cal/GM-° C;
Latent Heat: 5.78 Cal/GM; 24.2 J/GM;
|