| Specification |
Appearance: Water;
Application: Concrete Admixture;
Chemical Composition: Polycarboxylate Ether;
Setting Time: Normal Setting Time;
Type: High-range Water-reducing Agent;
Water Reduction Rate: 20%-30%;
Solid: 50%;
Fluidity: 0 Hour 205mm, 0.5h,185mm;
|
Appearance: Powder;
Application: Concrete Admixture, Floor Hardener, Grouting Material, Mortar Admixture, Plastering Material, Self-Leveling Compound, Construction Concrete Mixing;
Chemical Composition: Naphthalene Sulfonate Formaldehyde;
Setting Time: Normal Setting Time;
Type: High-range Water-reducing Agent;
Water Reduction Rate: 30%-40%;
Moisture Content (%): 0.8 Max;
Fineness 0.315mm Residue on Sieve (%): <15;
pH Value: 7-9;
Chloride(%): 0.2 Max;
Sodium Sulfate(%: 5 Max;
Total Alkali Quantity (%): 18 Max;
Insoluble (%): 0.5 Max;
Water Reduction(%): 17 Min;
Ratio of Bleeding(%): 80 Max;
Initial Setting: 90-120 Minuts;
Corrosion on Steel Bar: No;
Blend Dosage Range: 0.5-1.2%;
Packing, Transportation and Storage: 25 Kg or 50 Kg or 650 Kg;
After-Sales Service: Supply Usage Method.;
Usage: Long-Distance Construction Projects Type;
|
Appearance: Powder;
Application: Concrete Admixture, Floor Hardener, Grouting Material, Mortar Admixture, Plastering Material, Self-Leveling Compound, Construction Concrete Mixing;
Chemical Composition: Naphthalene Sulfonate Formaldehyde;
Setting Time: Normal Setting Time;
Type: High-range Water-reducing Agent;
Water Reduction Rate: 30%-40%;
Moisture Content (%): 0.8 Max;
Fineness 0.315mm Residue on Sieve (%): <15;
pH Value: 7-9;
Chloride(%): 0.2 Max;
Sodium Sulfate(%: 5 Max;
Total Alkali Quantity (%): 18 Max;
Insoluble (%): 0.5 Max;
Water Reduction(%): 17 Min;
Ratio of Bleeding(%): 80 Max;
Initial Setting: 90-120 Minuts;
Corrosion on Steel Bar: No;
Blend Dosage Range: 0.5-1.2%;
Packing, Transportation and Storage: 25 Kg or 50 Kg or 650 Kg;
After-Sales Service: Supply Usage Method.;
Usage: Self Compact Concrete;
|
Appearance: Brown Yellow Powder;
Application: Concrete Admixture, Grouting Material, Self-Leveling Compound;
Chemical Composition: Naphthalene Sulfonate Formaldehyde;
Setting Time: Rapid Setting Time;
Type: High-range Water-reducing Agent;
Water Reduction Rate: 12-20%;
|
Appearance: White Powder;
Application: Concrete Admixture, Grouting Material, Self-Leveling Compound;
Chemical Composition: Sulfonated Melamine Formaldehyde;
Setting Time: Rapid Setting Time;
Type: High-range Water-reducing Agent;
Water Reduction Rate: 10%-20%;
|