Specification |
Material: Natural Silica Mine;
Content: >90%;
Usage: Grind;
Processing Type: Grinding;
Size: 2-4cm, 4-6cm, 6-8cm, 8-10cm, 10-12cm, 12-15cm;
Color: White;
Sio2: >=99.31%;
Density: >=2.66~2.68g/cm3;
Hardness: >=8;
Fe2o3: <=0.018;
Al2O3: <=0.36%;
Shape: Round;
Item: Silica Pebbles Used for Ceramic Ball Mill Grinding;
|
Material: Alumina;
Content: >90%;
Usage: Machinery, Chemical, Petroleum;
Processing Type: Rolling Type;
Size: 6mm-75mm;
Color: White;
Customized: Customized;
Moh's Hardness Scale: 7.5;
Acid Resistance: 99.8% Min;
Character: Heat Resistance, Chemical Resistance;
Max. Operating Temperature: 1550;
|
Material: Zirconia;
Content: 95%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Grinding Ball;
Size: Small;
Color: White;
Customized: Customized;
Density: >3.2g/cm3;
Bulk Density: >2.0g/cm3;
Hardness: ≥9;
Abrasion: 2ppm%;
|
Material: Tc, Hard Metal, Hard Alloy, Tungsten Steel;
Content: Wc92%+Co8%;
Usage: Ball Mill, Roller Jar Mill, Attritors, Shaker Mill;
Processing Type: Sintering;
Size: 4,5,6,8,10,12,14,16,18,20mm etc. in Stock;
Color: Metallic;
Customized: Accepted;
Grade: Tungsten Carbide Mc8;
Grain Size: 1.2-1.6 μm;
Density: 14.7-14.78g/Cm³;
Hardness: 89.5-90.5hra;
Trs: >2300MPa;
Surface Finish: Unground;
Features: Resistant to Wear Corrosion and Impact;
|
Material: Zirconia;
Content: 95%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Grinding Ball;
Size: Small;
Color: White;
Customized: Customized;
Density: >3.2g/cm3;
Bulk Density: >2.0g/cm3;
Hardness: ≥9;
Abrasion: 2ppm%;
|