Specification |
CAS No.: 25068-38-6;
Formula: 231-072-3;
EINECS: C15h16o2c2h7onc3h5ocl;
Morphology: Water-Soluble;
Application: Construction, Woodworking;
Material: Epoxy;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: Clear;
Type: Double Components Adhesives;
Mixing Ratio: 3:1;
Life Time: Anti-Yellow at 5yrs+;
Grade: Food Grade FDA Approved;
Voc: 100% Solids, Low Voc, Low Odor;
Ripple: No Ripple, UV Resistant;
Leveling: Self-Leveling and Extremely Durable;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|