Specification |
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Volume Stability;
Production Process: Dry Pressing;
Refractoriness (℃): Refractoriness> 2000;
Shape: Board;
|
Feature: Good Acid Resistance, Good Mechanical Strength, Volume Stability;
Production Process: Dry Pressing;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block;
Sio2: ≥94.5%;
Al2O3: ≤2.0%;
Apparent Porosity: ≤24%;
Customized Package: Acceptable;
|
Sio2: ≥94.5%;
Al2O3: ≤2.0%;
Apparent Porosity: ≤24%;
Customized Product: Acceptable;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|