| Specification |
Color: White;
Al2O3: 47%;
Sio2: 51%;
Density: 200kg/M3;
Max Working Temperature: 1100c;
|
Material: Silicon Carbide Material;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Usage: Aerospace, Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Product Name: Silicon Carbide Ceramic Foam Filter;
Application: Grey Iron, Ductile Iron, Copper, Brass;
Refractoriness (ºC): Below 1500 Celsius;
Feature: Molten Metal Filtration;
Type: Refractory Material;
Size: 30mm-500mm, Customized;
Common Size: 40X40X15mm 50X50X15mm 50X50X22mm 50X75X22mm;
Pore Density: 10/15/20/25/30/40ppi (Ppi=Pores Per Inch);
Porosity(%): 80-90;
Bending Strength(MPa): >0.8;
Compression Strength(MPa): >1.0;
Thermal Sgock Resistance(Times/1100): 6;
Color: Grey;
|
Material: Silicon Carbide Material;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Usage: Aerospace, Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Product Name: Silicon Carbide Ceramic Foam Filter;
Application: Grey Iron, Ductile Iron, Copper, Brass;
Refractoriness (ºC): Below 1500 Celsius;
Feature: Molten Metal Filtration;
Type: Refractory Material;
Size: 30mm-500mm, Customized;
Common Size: 40X40X15mm 50X50X15mm 50X50X22mm 50X75X22mm;
Pore Density: 10/15/20/25/30/40ppi (Ppi=Pores Per Inch);
Porosity(%): 80-90;
Bending Strength(MPa): >0.8;
Compression Strength(MPa): >1.0;
Thermal Sgock Resistance(Times/1100): 6;
Color: Grey;
|
Material: Fiberglass;
Refractoriness (℃): 550c;
Surface Treatment: N/a;
Technique: Braided;
Temperature: 450°c-550°c;
Thickness: 3mm up to 50mm;
Roll Length: as Customers Request;
Color: Red;
|
Warp Density: 48~60 Piece/10cm;
High Temperature Tape: 1260c;
Thickness: 1.5mm-5.0mm;
Grade: HP (High Pure);
Chemical Composition: Ceramic Fiber;
Ultimate Strength (≥ MPa): 0.08-0.12;
Working Temperature: 1050c;
Fiber Diameter: 3-5um;
Color: White;
Thermal Conductivity: 0.20(1000c);
Shrinkage (1800ºF, 3h): -3;
|