Specification |
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 63-86;
Density,g/cm3: 1.06-1.12;
100% Modulus,MPa: 2.5-6;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 9-20;
Tear Strength,MPa: 35-75;
Elongation at Break,%: 700-950;
Tear Strength,Kn/M: 35-75;
|